エンジニアリングセラミックスメーカーであるクアーズテックが開発した石英ガラスレンズは、高純度な石英ガラス原料と独自のニアネットシェイプ法により3つの優れた特長を実現しています。
CoorsTek, an engineered ceramics manufacturer, has developed quartz glass lenses by combining high purity quartz glass material with original near-net-shape forming method based on ceramics manufacturing technology. The near-net-shape forming method enables quartz glass lenses features including:
CoorsTek, an engineered ceramics manufacturer, has developed quartz glass lenses by combining high purity quartz glass material with original near-net-shape forming method based on ceramics manufacturing technology. The near-net-shape forming method enables quartz glass lenses features including:
レンズアレイ
キャップ形状(中空)レンズ
- 光学特性に優れ、UV波長領域においても高い透過率を実現
-
Excellent optical properties and high transmittance in the UV wavelength region
- 形状自由度が高く複雑形状への対応が可能
-
Higher degree of freedom of shape-creation which enables production of complex shapes
- 仕上加工が不要なため低コストで製造可能
-
No finishing process is required which enables cost-effective production
- 形状
-
対応形状はレンズアレイ、フランジ付レンズなど多様な形状を作製可能です。
UV-LED用レンズをはじめ様々な光学部材としてお使い頂けます。
Quartz glass lenses are available in several shapes for various applications including UV-LED lenses and small optical parts. Available shapes: Lens array, Lens with flange etc.
フランジ付きレンズ
キャップ形状(中空)レンズ
レンズアレイ(丸タイプ)
レンズアレイ（六方細密タイプ）
シリンドリカルレンズ
フレネルレンズ
- ニアネットシェイプ法
-
ニアネットシェイプ法とは型を用いて複雑な形状を成形し、離型後の収縮や変形を適切に制御することで仕上加工を行うことなく完成製品を得る製造方法です。従来の石英ガラスレンズはインゴットからの削り出しによって製造するため形状自由度が低く価格が高いのが一般的でしたが、クアーズテックの石英ガラスレンズはニアネットシェイプ法によりこれらの問題を解決しました。
The near-net-shape forming method is a manufacturing technique for producing complex shaped bodies using a mold. After demolding, shrinkage and deformation factors are properly controlled to obtain a completed shape without finishing process. Since conventional Quartz glass lenses are produced by cutting out from an ingot, the degree of freedom of shape-creation is low and the cost is high. However, CoorsTek has solved the tasks by creating complex shaped quartz glass lenses using a near-net-shape forming method.
- 光透過率
-
クアーズテックの石英ガラスレンズはUV波長領域においてもほとんど吸収が無く、合成石英ガラス並みの高い透過率を実現しています。波長265nmにおける透過率は92％(板厚4mm)になります。
CoorsTek quartz glass lens has no absorption in the UV wavelength region and optical transmittance at 265nm is 92% (thickness4mm) which is very similar to synthetic quartz.
- 深紫外線耐性
-
クアーズテックの石英ガラスレンズは深紫外線耐性に優れており、UV照射1000時間後も透過率に変化はありません。
CoorsTek quartz glass lens has excellent UV resistance and shows almost no change in its transmittance even after 1000 hours of UV irradiation test.
- 主要物性値
-
Main physical properties
- LED用
-
LED用カバーガラス、レンズ付きカバーガラス、蓋(Lid)や透過窓(Transparent window)
- アレイLED用
-
アレイLED用カバーガラス、レンズ付きカバーガラス(レンズアレイ)、蓋や透過窓
- 受光センサー用
-
受光センサー用のカバーガラス、蓋や透過窓
- 殺菌装置用
-
水/液体、空気、表面殺菌用装置のレンズや透過窓
(COVID19などのコロナウイルス、インフルエンザおよび各種細菌の殺菌デバイス用レンズなど)
- 医療用
-
医療用(アトピー、皮膚炎治療、歯科治療)装置のレンズや透過窓
- その他用途
-
紫外線洗浄、分析、選別、接着、加工、印刷用装置のレンズや透過窓